Adsorption performance and optimization by response surface methodology on tetracycline using Fe-doped ZIF-8-loaded...

Herein, an iron-doped ZIF-8-loaded multi-walled carbon nanotube (FZM) was synthesized and its adsorption performance on tetracycline (TC) was investigated. The experimental conditions (solution pH, temperature, adsorbent dose) were optimized by Box-Behnken design (BBD) in response surface methodology (RSM). The results show that the adsorption effect of TC by FZM is optimal under the conditions of temperature = 298 K, pH = 6, and contact time = 360 min. The adsorption processes of TC by FZM follow the pseudo-second-order (PSO) kinetic and Freundlich isotherm models, indicating that chemisorption is the dominant factor and the adsorption reaction is multi-layer, with a theoretical maximum saturation capacity of 1111.11 mg/g at 298 K. The adsorption thermodynamic results indicate that the adsorption of TC by FZM is a spontaneous and endothermic process. The mechanism of TC adsorption by FZM possibly occurs through hydrogen bonding, surface complexation, π-π interaction, and electrostatic interaction. From the statistical results, the optimal adsorption capacity of TC by FZM is 599.78 mg/g at a pH of 7.1, a temperature of 312.5 K, and an adsorbent dose of 64.43 mg/L, with a deviation of 1.73% from the actual value. Furthermore, regeneration experiments demonstrate that FZM has excellent reusability with a 15% loss of adsorption capacity after four cycles. This study provides some insights to study the adsorption behavior of TC by MOFs and the optimization of the adsorption experimental conditions, and also shows the potential of FZM for TC removal.