Poly(Butylene Adipate/Terephthalate-Co-Glycolate) Copolyester Synthesis Based on Methyl Glycolate with Improved...

The main problem of manufacturing with traditional biodegradable plastics is that it is more expensive than manufacturing with polymers derived from petroleum, and the application scope is currently limited due to poor comprehensive performance. In this study, a novel biodegradable poly(butylene adipic acid/terephthalate-co-glycolic acid) (PBATGA) copolyester with 25-60% glycolic acid units was successfully synthesized by esterification and polycondensation using cheap coal chemical byproduct methyl glycolate instead of expensive glycolic acid. The structure of the copolyester was characterized by ATR-FTIR, ¹H NMR, DSC, and XRD; and its barrier property, water contact angle, heat resistance, and mechanical properties were tested. According to the experiment result, the PBATGA copolyesters showed improved oxygen (O₂) and water vapor barrier character, and better hydrophilicity when compared with PBAT. The crystallization peaks of PBATGAs were elevated from 64 °C to 77 °C when the content of the GA unit was 25 mol %, meanwhile, the elongation at the break of PBATGA25 was more than 1300%. These results indicate that PBATGA copolyesters have good potentiality in high O₂ and water vapor barrier and degradable packaging material.