Study on Symmetry and Asymmetry Rolling of AA2519-T62 Alloy at Room-Temperature and Cryogenic Conditions

The aim of this investigation was to identify the effect of rolling at room temperature and under cryogenic conditions on selected properties and the microstructure of the AA2519-T62 aluminum alloy. The rolling processes were conducted with different variants of asymmetry (1.0-symmetry rolling; 1.2, 1.4 and 1.6). The investigation of the obtained samples involves microhardness distribution, microstrains, and microstructure observations using light and transmission electron microscopes. Both rolling at room temperature and under cryogenic conditions increased the micro-hardness of AA2519-T62 by at least 10%. The highest reported increase (25%) was obtained for the sample rolled at room temperature in the symmetry rolling process. The samples rolled under cryogenic conditions are characterized by a lower increase in microhardness than samples rolled at room temperature and by significantly lower values of microstrains. The application of rolling with the asymmetry ratio remaining within the range of 1.2-16 only slightly affected the microhardness values of the samples rolled at room temperature and under cryogenic conditions with respect to conventional symmetrical rolling.