Synthesis and Properties of Polyol Copolymer with Alternating Methacrylate-Vinyl Ether Backbone

Radical polymerization of a tailored diphenylsilane-bridged bi-functional monomer consisting of methacrylate and vinyl ether moieties is conducted in diluted monomer concentration, in which both two moieties are consumed at almost the same rate despite their huge difference in monomer reactivity ratio. The vinyl ether content in the backbone is quantified as 45% by ¹ H NMR after removal of the silane bridge. Since vinyl ether alone cannot be polymerized in such radical polymerization, it should be incorporated in an alternating fashion with methacrylate into the copolymer main chain. The cleavage of silane bridge also yields a series of polyol materials composed of ethylene glycol monovinyl ether (EGVE) and hydroxyethyl methacrylate (HEMA), and the EGVE content in the backbone can be regulated from 45% to 18% by increasing the bi-functional monomer concentration. Interestingly, although containing more than 50% HEMA units, the alternating copolymer exhibits new properties totally different from poly(HEMA), but more similar to poly(EGVE), e.g., good water solubility and a markedly low glass transition temperature (T_g ) of -31 °C, which is attributed to the major HEMA-EGVE repeating unit that replaced HEMA-HEMA consecutive segments so that the properties of poly(HEMA) such as 95 °C T_g are completely altered.