Polymerization shrinkage of light-cured conventional and bulk-fill composites -The effect of cavity depth and...

Volumetric shrinkage (VS) of conventional, bulk-fill, and core build-up resin-based composites (RBCs) of various thickness (1-5 mm) was measured using the modified bonded-disk method with confocal laser scanning microscopy. Additionally, the bottom-to-top ratio of Vickers hardness (%VH) was measured. Conventional RBCs exhibited significantly higher VS than bulk-fill and core build-up RBCs (p<0.05). As specimen thickness increased, VS relative to volume (%VS) and difference in VS at each depth (VS_depth) decreased. For conventional RBCs, there was a significant drop in VS_depth between 1 mm and 2 mm (p<0.05), and another drop was observed between 3 mm and 4 mm (p<0.05) where %VH decreased below 90%. For bulk-fill and core build-up RBCs, VS_depth decreased significantly between 2 mm and 3 mm (p<0.05), but %VH exceeded 90% even in 5 mm deep cavities. These results indicated that post-curing contributed to lower shrinkage in deeper layers, and that conventional RBCs were not adequately polymerized at the depth of over 3 mm.