High-Throughput Area-Selective Spatial Atomic Layer Deposition of SiO₂ with Interleaved Small Molecule Inhibitors and...

A first-of-its-kind area-selective deposition process for SiO₂  is developed consisting of film deposition with interleaved exposures to small molecule inhibitors (SMIs) and back-etch correction steps, within the same spatial atomic layer deposition (ALD) tool. The synergy of these aspects results in selective SiO₂  deposition up to ~23 nm with high selectivity and throughput, with SiO₂  growth area and ZnO nongrowth area. The selectivity is corroborated by both X-ray photoelectron spectroscopy (XPS) and low-energy ion scattering spectroscopy (LEIS). The selectivity conferred by two different SMIs, ethylbutyric acid, and pivalic acid has been compared experimentally and theoretically. Density Functional Theory (DFT) calculations reveal that selective surface functionalization using both SMIs is predominantly controlled thermodynamically, while the better selectivity achieved when using trimethylacetic acid can be explained by its higher packing density compared to ethylbutyric acid. By employing the trimethylacetic acid as SMI on other starting surfaces (Ta₂ O₅ , ZrO₂ , etc.) and probing the selectivity, a broader use of carboxylic acid inhibitors for different substrates is demonstrated. It is believed that the current results highlight the subtleties in SMI properties such as size, geometry, and packing, as well as interleaved back-etch steps, which are key in developing ever more effective strategies for highly selective deposition processes.