Multiwalled Carbon Nanotubes-Modified Metallic Electrode Prepared Using Chemical Vapor Deposition as Sequential...

A carbon nanotubes modified silver electrode (CNTs-Ag) was prepared via catalytic chemical vapor deposition and characterized. The morphology, crystallinity, elemental composition, and other quality parameters of the prepared electrode were investigated using scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Raman techniques. The characterization results revealed the modification of the silver metal surface with CNTs of good characteristics. A sequential injection analysis (SIA) system was developed for studying the reaction of ascorbic acid with KIO₃ using the prepared CNTs-Ag electrode. Electrodes were polarized with both direct current (DC) and periodic square wave (SW). Various experimental conditions affecting the differential electrolytic potentiometric (DEP) peak such as current density, SW bias value, and flow rate were appraised. Under the optimum conditions, good linear responses for ascorbic acid were obtained in the range of 60.0-850.0 µM for both types of polarization with detection limits of 14.0-19.0 µM. The results obtained showed that the periodic polarization method was more sensitive than DC polarization and the electrode response was faster. Ascorbic acid in pharmaceutical tablets was determined with satisfactory results using this method. The prepared CNTs-based electrode exhibited good performance for a long period of use. The method is simple, rapid, and inexpensive for routine analysis.