Three-Dimensional-Printed Molds from Water-Soluble Sulfate Ceramics for Biocomposite Formation through Low-Pressure...

Powder mixtures of MgSO₄ with 5-20 mol.% Na₂SO₄ or K₂SO₄ were used as precursors for making water-soluble ceramic molds to create thermoplastic polymer/calcium phosphate composites by low pressure injection molding. To increase the strength of the ceramic molds, 5 wt.% of tetragonal ZrO₂ (Y₂O₃-stabilized) was added to the precursor powders. A uniform distribution of ZrO₂ particles was obtained. The average grain size for Na-containing ceramics ranged from 3.5 ± 0.8 µm for MgSO₄/Na₂SO₄ = 91/9% to 4.8 ± 1.1 µm for MgSO₄/Na₂SO₄ = 83/17%. For K-containing ceramics, the values were 3.5 ± 0.8 µm for all of the samples. The addition of ZrO₂ made a significant contribution to the strength of ceramics: for the MgSO₄/Na₂SO₄ = 83/17% sample, the compressive strength increased by 49% (up to 6.7 ± 1.3 MPa), and for the stronger MgSO₄/K₂SO₄ = 83/17% by 39% (up to 8.4 ± 0.6 MPa). The average dissolution time of the ceramic molds in water did not exceed 25 min.