Preparation and Lithium-Ion Separation Property of ZIF-8 Membrane with Excellent Flexibility

Metal-organic framework (MOF) membranes exhibit immense potential for separation applications due to their regular pore channels and scalable pore sizes. However, structuring a flexible and high-quality MOF membrane remains a challenge due to its brittleness, which severely restricts its practical application. This paper presents a simple and effective method in which continuous, uniform, defect-free ZIF-8 film layers of tunable thickness are constructed on the surface of inert microporous polypropylene membranes (MPPM). To provide heterogeneous nucleation sites for ZIF-8 growth, an extensive amount of hydroxyl and amine groups were introduced on the MPPM surface using the dopamine-assisted co-deposition technique. Subsequently, ZIF-8 crystals were grown in-situ on the MPPM surface using the solvothermal method. The resultant ZIF-8/MPPM exhibited a lithium-ion permeation flux of 0.151 mol m^-2 h^-1 and a high selectivity of Li⁺/Na⁺ = 1.93, Li⁺/Mg²⁺ = 11.50. Notably, ZIF-8/MPPM has good flexibility, and the lithium-ion permeation flux and selectivity remain unchanged at a bending curvature of 348 m^-1. These excellent mechanical characteristics are crucial for the practical applications of MOF membranes.