Influence of Pretreatment Methods on Compressive Performance Improvement and Failure Mechanism Analysis of Recycled...

The utilization of recycled aggregate can avert the squandering of resources and the destruction of the environment. Nevertheless, there exists a slew of old cement mortar and microcracks on the surface of recycled aggregate, which give rise to the poor performance of aggregates in concrete. In this study, for the sake of ameliorating this property of recycled aggregates, the surface of the recycled aggregates is covered with a layer of cement mortar to compensate for the microcracks on the surface and reinforce the bond between old cement mortar and aggregates. In order to demonstrate the influence of recycled aggregate by different cement mortar pretreatment methods, this study prepared natural aggregate concrete (NAC) and concretes with recycled aggregate after the wetting pretreatment (RAC-W) and cement mortar pretreatment (RAC-C), and conducted uniaxial compressive strength tests on different types of concrete at different curing ages. The test results indicated that the compressive strength of RAC-C at a 7 d curing age was higher than that of RAC-W and NAC, and the compressive strength of RAC-C at a 28 d curing age was higher than RAC-W but lower than NAC. The compressive strength of NAC and RAC-W at a 7 d curing age was about 70% of that at a 28 d curing age, and the compressive strength of RAC-C at a 7 d curing age was about 85-90% of that at a 28 d curing age. The compressive strength of RAC-C increased dramatically at the early stage, while the post-strength of the NAC and RAC-W groups increased rapidly. The fracture surface of RAC-W mainly occurred in the transition zone between the recycled aggregates and old cement mortar under the pressure of the uniaxial compressive load. However, the main failure of RAC-C was the crushing destruction of cement mortar. With changes in the amount of cement added beforehand, the proportion of aggregate damage and A-P interface damage of RAC-C also changed accordingly. Therefore, the recycled aggregate pretreated with cement mortar can significantly improve the compressive strength of recycled aggregate concrete. The optimal amount of pre-added cement was 25%, which is recommended for practical engineering.