Effect of Crosshead Speed and Volume Ratio on Compressive Mechanical Properties of Mono- and Double-Gyroid Structures...

The current development of additive technologies brings not only new possibilities but also new challenges. One of them is the use of regular cellular materials in various components and constructions so that they fully utilize the potential of porous structures and their advantages related to weight reduction and material-saving while maintaining the required safety and operational reliability of devices containing such components. It is therefore very important to know the properties of such materials and their behavior under different types of loads. The article deals with the investigation of the mechanical properties of porous structures made by the Direct Metal Laser Sintering (DMLS) of Inconel 718. Two types of basic cell topology, mono-structure Gyroid (G) and double-structure Gyroid + Gyroid (GG), with material volume ratios of 10, 15 and 20 %, were studied within our research to compare their properties under quasi-static compressive loading. The testing procedure was performed at ambient temperature with a servo-hydraulic testing machine at three different crosshead testing speeds. The recorded data were processed, while the stress-strain curves were plotted, and Young's modulus, the yield strength Re_0.2, and the stress at the first peak of the local maximum σ_LocMax were identified. The results showed the best behavior under compression load among the studied structures displayed by mono-structure Gyroid at 10 %. At the same time, it can be concluded that the wall thickness of the structure plays an important role in the compressive properties but on the other hand, crosshead speed doesn´t influence results significantly.