The biomechanical stability of miniplate osteosynthesis configurations in bilateral mandibular angle fractures

The present study investigated the biomechanical stability of three miniplate osteosynthesis configurations used for internal fixation of bilateral mandibular angle fracture (BMAF).

Standard fracture lines were created in 72 polyurethane mandibles and stabilized with 2.0-mm, 4-hole standard titanium miniplates and monocortical screws. The group descriptions and miniplate configurations were: 2Plates (1-1), 3Plates (1-2) and 4Plates (2-2). The mandibles were subjected to either incisal or molar loads (from both sides in the 3Plates group) up to a force of 120 N. The displacements of the constructs were recorded at each force increment of 10 N. ANOVA and Tukey's post-hoc tests were used for statistical analysis.

The 2Plates group showed higher displacement under both loading conditions (P < 0.05 for each). The same group reached displacement levels of 1 mm and 3 mm during molar loading and 1 mm, 3 mm, and 5 mm during incisal loading at lower force magnitudes relative to others (P < 0.05 for each).

Bone-plate constructs for BMAFs stabilized with three or four standard miniplates are more likely to provide similar resistance when subjected to incisal or molar loads, in contrast to the two-miniplate configuration, which is relatively more prone to displacement.