Hierarchical Multiple Precursors Induced Heterogeneous Structures in Super Austenitic Stainless Steels by Cryogenic...

Multiple deformed substructures including dislocation cells, nanotwins (NTs) and martensite were introduced in super austenitic stainless steels (SASSs) by cryogenic rolling (Cryo-R, 77 K/22.1 mJ·m^-2). With the reduction increasing, a low stacking fault energy (SFE) and increased flow stress led to the activation of secondary slip and the occurrence of NTs and martensite nano-laths, while only dislocation tangles were observed under a heavy reduction by cold-rolling (Cold-R, 293 K/49.2 mJ·m^-2). The multiple precursors not only possess variable deformation stored energy, but also experience competition between recrystallization and reverse transformation during subsequent annealing, thus contributing to the formation of a heterogeneous structure (HS). The HS, which consists of bimodal-grained austenite and retained martensite simultaneously, showed a higher yield strength (~1032 MPa) and a larger tensile elongation (~9.1%) than the annealed coarse-grained Cold-R sample. The superior strength-ductility and strain hardening originate from the synergistic effects of grain refinement, dislocation and hetero-deformation-induced hardening.