Antibacterial, antioxidant and fruit packaging ability of biochar-based silver nanoparticles-polyvinyl...

Silver nanoparticles were prepared by loading Ag⁺ into biochar of waste barley distillers' grains shell by reduction with trisodium citrate, and this silver-loaded biochar was introduced into polyvinyl alcohol-chitosan. Various analysis with Fourier Transform Infrared spectroscopy, X-ray diffraction, Thermogravimetric analysis, and water contact angle revealed that biochar-based silver nanoparticle was incorporated into the polyvinyl alcohol-chitosan film, the biochar-based silver nanoparticles-polyvinyl alcohol-chitosan (C-Ag-loaded PVA/CS) composite film had good thermostability and hydrophobicity. Through the analysis via disk diffusion method, the composite containing 3 % of biochar-based silver nanoparticles-polyvinyl alcohol-chitosan had high antibacterial activity (inhibition zone: 18 mm against E. coli and 15 mm against S. aureus), and the bacterial membrane permeability was measured, indicating that C-Ag-loaded PVA/CS composite film could destroy the cell membrane, release intracellular substances, and have high antioxidant activity. During the storage, the weight loss rate of the biochar-based silver nanoparticles-polyvinyl alcohol-chitosan plastic wrap group was 0.14 %, and the titratable acid content only decreased by 0.061 %, which had a good effect on extending the shelf life of blueberries. The C-Ag-loaded PVA/CS composite film could also delay deterioration of blueberries and prolong storage time. Overall, this composite film had potential in food packaging and extending food shelf-life aspects.