Zinc oxide nanoparticle-reinforced pectin/starch functionalized films: A sustainable solution for biodegradable...

Environmental pollution caused by non-biodegradable plastic pollutants adversely affects various ecosystems. This study proposes the development of novel functional and biodegradable films based on corn starch (CST) and pectin (PEC) containing zinc oxide nanoparticles (ZnONPs) from the casting method. The films exhibited processability, transparency, low water vapor permeation, and desirable mechanical properties for food packaging and coating applications. The ZnONPs acted as a plasticizer, enhancing the film elongation at the break, increasing the pec25-1 (PEC 25 wt% and ZnONPs 1 wt%) elongation from 79.85 to 162.32 %. The improved film elasticity supported by ZnONPs reduced the material stiffness. However, the films still demonstrated an average tensile strength (0.69 MPa) 17-fold higher than the tensile strength (0.04 MPa) of the non-biodegradable commercial film based on poly(vinyl chloride). Furthermore, the ZnONPs enhanced the UV-blocking capabilities of the films, leading to wettable materials with water contact angles lower than 90°. The films showed high biodegradation rates under natural disposal conditions. The results indicated that the pec25-1/ZnONPs film is a promising eco-friendly coating in food preservation due to its biodegradability, suitable mechanical properties, low water vapor permeability, and UV-blocking properties.