Ti₃C₂T MXene-based hybrid nanocoating for flame retardant, early fire-warning and piezoresistive tension sensing...

Flammability feature of textiles is a big underlying risk causing fire disasters. The fabrication of reliable fire resistant and quick fire warning fabrics is imperative but challenging. Herein, three types of early fire-warning polyester fabrics, namely, FPP@AM-X, FPP@PM-X and FPP@AX-M1, with good flame retardant and piezoresistive sensing performance were developed by fabricating polyethyleneimine (PEI), ammonium polyphosphate (APP), phytic acid (PA) and MXenes onto phosphorus-containing flame retardant polyethylene terephthalate (FRPET) via polydopamine (PDA) mediated layer-by-layer self-assembly. Owing to the improved thermoelectric properties of MXenes, FPP@A5-M1 exhibited a maximum thermoelectric voltage of 0.59 mV at a temperature difference of 130 °C and can provide an ideal cyclic early fire warning response within 4 s. In addition, due to the synergistic flame retardant effect of MXenes and APP in the coating layer, FPP@A5-M1 could be self-extinguished within 2 s after ignition and the value of peak heat release ratio and total smoke production decreased by 41.9% and 30.4%, respectively. Besides, the MXene-based hybrid coated fabric can detect the movement of human fingers and elbows, illustrating its potential application in piezoresistive tension sensing. This work provides a new route to designing and developing multi-functional and smart fire protection fabrics.