A novel porous titanium with engineered surface for bone defect repair in load-bearing position

Porous titanium exhibits low elastic modulus and porous structure is thought to be a promising implant in bone defect repair. However, the bioinert and low mechanical strength of porous titanium have limited its clinical application, especially in load-bearing bone defect repair. Our previous study has reported an infiltration casting and acid corrosion (IC-AC) method to fabricate a novel porous titanium (pTi) with 40% porosity and 0.4 mm pore diameter, which exerts mechanical property matching with cortical bone and interconnected channels. In this study, we introduced a nanoporous coating and incorporated an osteogenic element strontium (Sr) on the surface of porous titanium (named as Sr-micro arch oxidation [MAO]) to improve the osteogenic ability of the pTi by MAO. Better biocompatibility of Sr-MAO was verified by cell adhesion experiment and cell counting kit-8 (CCK-8) test. The in vitro osteogenic-related tests such as immunofluorescence staining, alkaline phosphatase staining and real-time polymerase chain reaction (RT-PCR) demonstrated better osteogenic ability of Sr-MAO. Femoral bone defect repair model was employed to evaluate the osseointegration of samples in vivo. Results of micro-CT scanning, sequential fluorochrome labeling and Van Gieson staining suggested that Sr-MAO showed better in vivo osteogenic ability than other groups. Taking results of both in vitro and in vivo experiment together, this study indicated the Sr-MAO porous titanium could be a promising implant load-bearing bone defect.