Effects of Polybutylene Succinate Content on the Rheological Properties of Polylactic Acid/Polybutylene Succinate...

Polylactic acid (PLA) and polybutylene succinate (PBS) are gaining prominence as environmentally friendly alternatives to petroleum-based polymers due to their inherent biodegradability. For their textile applications, this research is focused on exploring the effects of PBS content on the rheological properties of PLA/PBS blends and the characteristics of PLA/PBS blend fibers. PLA/PBS blends and fibers with varying PBS contents (0 to 10 wt.%) were prepared using melt-blending and spinning methods. Uniform morphologies of the PLA/PBS blends indicated that PBS was compatible with PLA, except at 10% PBS content, where phase separation occurred. The introduction of PBS reduced the complex viscosity of the blends, influencing fiber properties. Notably, PLA/PBS fibers with 7% PBS exhibited improved crystallinity, orientation factor, and elasticity (~16.58%), with a similar tensile strength to PLA fiber (~3.58 MPa). The results suggest that an optimal amount of PBS enhances alignment along the drawing direction and improves the molecular motion in PLA/PBS blend fiber. This study highlights the potential of strategically blending PBS to improve PLA fiber characteristics, promising advancement in textile applications.