Manufacturing Autoclave-Grade Thermoset Carbon Fiber-Reinforced Polymer Aerospace Composites without an Autoclave...

Composite laminates utilizing autoclave-grade carbon fiber-reinforced plastic (CFRP) prepreg were manufactured using a polymer nanoporous network (NPN) interlayer that generates capillary pressure in lieu of pressure from an autoclave. The polymer nanofiber NPN film is integrated into the interlaminar region and is shown to eliminate voids in a vacuum-bag-only (VBO) curing process. After a preliminary investigation of the effect of NPN thickness on the interlaminar region and performance, an 8 μm thick polymer NPN was selected for a scaled manufacturing demonstration. Combining the polymer NPN with "out-of-oven" (OoO) electrothermal heating of a carbon nanotube (CNT)-heated tool, a 0.6 × 0.6 m void-free plate is successfully manufactured. OoO cure enables an accelerated cure cycle, which reduces the cure time by 35% compared to the manufacturer-recommended cure cycle (MRCC). X-ray microcomputed tomography (μ-CT) reveals that the laminates are void-free and of identical quality to autoclave-cured specimens. An array of mechanical tests including tension, compression, open-hole compression (OHC), tension-bearing (bolt-bearing), and compression after impact, reveal that the accelerated NPN-cured composites were broadly equivalent, with some instances of improved properties, relative to the autoclave-cured parts, e.g., OHC strength increased by 5%. With reduced capital costs, energy consumption, and increased throughput, the facile polymer NPN-enabled out-of-autoclave (OoA) fabrication method is shown to be a practical and attractive alternative to conventional autoclave fabrication.