Evaluation of Osteogenic Potential of a Polysaccharide-Based Hydrogel Coating on Titanium

Reducing the healing period after surgical placement of dental implants can facilitate the loading of dental prostheses.

The aim is to compare the osteogenic potential of unmodified titanium disks with titanium disks that were surface-modified or hydrogel-coated.

One hundred eight titanium disks (Ø6 × 2-mm) were divided into three groups: (1) unmodified titanium as control (Ti-C); (2) sandblasted and acid-etched (Ti-SLA), and (3) coated with tamarind kernel polysaccharide hydrogel grafted with acrylic acid (Ti-TKP-AA). The osteogenic potential and cytotoxic effect of various groups of titanium were compared using human osteoblasts Saos-2. The surface topography of the titanium disks and morphology of osteoblasts grown on disks were investigated by scanning electron microscopy (n = 3). Cell attachment to the disks and actin expression intensity were investigated by confocal imaging (n = 3). Cytotoxicity was quantified by cell viability assay (n = 9). Osteoblast maturation was determined by alkaline phosphatase assay (n = 9). Cell mineralization was quantified by Alizarin red staining (n = 9). One-way analysis of variance followed by Tukey's multiple comparisons test was used for intergroup comparisons (α= 0.05).

The surface modifications on Ti-SLA and Ti-TKP-AA support better morphology and proliferation of osteoblasts than Ti-C (P< 0.001) and significantly higher levels of actin cytoskeleton accumulation (P< 0.0001). Ti-TKP-AA showed a significantly higher maturation rate than Ti-C (P< 0.001). Ti-TKP-AA showed > twofold increased mineralization than Ti-C and Ti-SLA (P< 0.001).

TKP-AA hydrogel-coated titanium promotes faster osteoblast proliferation, maturation, and mineralization than SLA-treated or untreated titanium. These advantages can be explored for achieving early osseointegration and prosthetic loading of titanium dental implants.