Properties and release behavior of sodium alginate-based nanocomposite active films: Effects of particle size of IRMOF-3

Nanoparticles are used as fillers to improve the properties of biopolymers, and their particle size is an important parameter. This work aims to investigate the effect of particle size of isoreticular metal-organic framework-3 (IRMOF-3) on the mechanical, physical, and release properties of sodium alginate (SA)-based composite active film. In our study, IRMOF-3 with six different particle sizes was synthesized by introducing additives. IRMOF-3 loading with carvacrol (IRMOF-3/CA nanoparticles) was incorporated into the SA matrix to prepare the composite film. The characterization and testing results of films showed that the particle size of nanoparticles affected the physical morphology and chemical structure of the film. Especially smaller nanoparticles uniformly dispersed into the SA matrix more easily, forming a denser and more stable spatial network structure with SA, which could more significantly improve the tensile strength, water vapor barrier, and hydrophobic properties of the film (P < 0.05). In addition, the CA release rate from the active film could be significantly reduced by about 33.90 % even when the smallest particle size of the IRMOF-3/CA nanoparticles was added. Therefore, when IRMOF-3/CA is used as the nano-filler to develop SA-based active film, its particle size has a potential influence on the properties of the film.