Multicolor Inks of Black Phosphorus for Midwave-Infrared Optoelectronics

Black phosphorus (bP) based ink with a bulk bandgap of 0.33 eV (λ = 3.7 µm) has recently been shown to be promising for large-area, high performance mid-wave infrared (MWIR) optoelectronics. However, the development of multicolor bP inks expanding across the MWIR wavelength range has been challenging. Here a multicolor ink process based on bP with spectral emission tuned from 0.28 eV (λ = 4.4 µm) to 0.8 eV (λ = 1.5 µm) is demonstrated. Specifically, through the reduction of bP particle size distribution (i.e., lateral dimension and thickness), the optical bandgap systematically blueshifts, reaching up to 0.8 eV. Conversely, alloying bP with arsenic (bP_{1- x}As_x) induces a redshift in the bandgap to 0.28 eV. The ink processed films are passivated with an infrared-transparent epoxy for stable infrared emission in ambient air. Utilizing these multicolor bP-based inks as an infrared light source, a gas sensing system is demonstrated that selectively detects gases, such as CO₂ and CH₄ whose absorption band varies around 4.3 and 3.3 µm, respectively. The presented ink formulation sets the stage for the advancement of multiplex MWIR optoelectronics, including spectrometers and spectral imaging using a low-cost material processing platform.