Properties of Biocomposites Made of Extruded Apple Pomace and Potato Starch: Mechanical and Physicochemical...

This paper presents research results on biocomposites made from a combination of extruded apple pomace (EAP) and potato starch (SP). The aim of this work was to investigate the basic properties of biocomposites obtained from extruded apple pomace reinforced with potato starch. The products were manufactured by hot pressing using a hydraulic press with a mould for producing samples. The prepared biocomposites were subjected to strength tests, surface wettability was determined, and a colour analysis was carried out. A thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), and cross-sectioning observed in a scanning electron microscope (SEM) were also performed. The obtained test results showed that the combination of apple pomace (EAP) and starch (SP) enabled the production of compact biocomposite materials. At the same time, it was found that each increase in the share of starch in the mixture for producing biocomposites increased the strength parameters of the obtained materials. With the highest share of starch in the mixture, 40%, and a raw material moisture content of 14%, the material had the best strength parameters and was even characterised by hydrophobic properties. It was also found that materials with a high content of starch are characterised by increased temperature resistance. The analysis of SEM microscopic photos showed well-glued particles of apple pomace, pectin, and gelatinised starch and a smooth external structure of the samples. Research and analyses have shown that apple pomace reinforced only with the addition of starch can be a promising raw material for the production of simple, biodegradable biocomposite materials.