Experimental investigation on the macro- and micromechanical properties of water-cooled granite at different high...

To investigate the damage mechanisms in granite's physical and mechanical properties after high-temperature water quenching, this study employed MTS815.04 for uniaxial compression tests on thermally treated specimens, with concurrent acoustic emission monitoring, and utilized nanoindentation for micromechanical analysis. The results show that with increasing temperature, granite's peak strength and elastic modulus decrease, with a sharp decline after 400-500 °C, corresponding to a significant increase in the internal damage, which can be detected by acoustic emission monitoring. Below 500 °C, macroscopic mechanical degradation is due to mineral thermophysical property differences, while above 500 °C, microcrack development is the main deterioration factor. The failure mode shifts from tensile to tensile-shear complex to shear failure, with transition points at 400 °C and 800 °C. The results of this study are of certain reference value for improving the efficiency of extracting thermal energy from dry-hot rocks and providing security guidance for the tunnel restoration process following fire damage.