Physical Properties of an Efficient MAPbBr₃/GaAs Hybrid Heterostructure for Visible/Near-Infrared Detectors

Semiconductor photodetectors can work only in specific material-dependent light wavelength ranges, connected with the bandgaps and absorption capabilities of the utilized semiconductors. This limitation has driven the development of hybrid devices that exceed the capabilities of individual materials. In this study, for the first time, a hybrid heterojunction photodetector based on methylammonium lead bromide (MAPbBr₃) polycrystalline film deposited on gallium arsenide (GaAs) was presented, along with comprehensive morphological, structural, optical, and photoelectrical investigations. The MAPbBr₃/GaAs heterojunction photodetector exhibited wide spectral responsivity, from 540 to 900 nm. The fabrication steps of the prototype device, including a new preparation recipe for the MAPbBr₃ solution and spinning, will be disclosed and discussed. It will be shown that extending the soaking time and refining the precursor solution's stoichiometry may enhance surface coverage, adhesion to the GaAs, and film uniformity, as well as provide a new way to integrate MAPbBr₃ on GaAs. Compared to the pristine MAPbBr₃, the enhanced structural purity of the perovskite on GaAs was confirmed by X-ray Diffraction (XRD) upon optimization compared to the conventional glass substrate. Scanning Electron Microscopy (SEM) revealed the formation of microcube-like structures on the top of an otherwise continuous MAPbBr₃ polycrystalline film, with increased grain size and reduced grain boundary effects pointed by Energy-Dispersive Spectroscopy (EDS) and cathodoluminescence (CL). Enhanced absorption was demonstrated in the visible range and broadened photoluminescence (PL) emission at room temperature, with traces of reduction in the orthorhombic tilting revealed by temperature-dependent PL. A reduced average carrier lifetime was reduced to 13.8 ns, revealed by time-resolved PL (TRPL). The dark current was typically around 8.8 × 10^-8 A. Broad photoresponsivity between 540 and 875 nm reached a maximum of 3 mA/W and 16 mA/W, corresponding to a detectivity of 6 × 10¹⁰ and 1 × 10¹¹ Jones at -1 V and 50 V, respectively. In case of on/off measurements, the rise and fall times were 0.40 s and 0.61 s or 0.62 s and 0.89 s for illumination, with 500 nm or 875 nm photons, respectively. A long-term stability test at room temperature in air confirmed the optical and structural stability of the proposed hybrid structure. This work provides insights into the physical mechanisms of new hybrid junctions for high-performance photodetectors.