Mechanical Characterization of Flax and Hemp Fibers Cultivated in Romania

This study examines the mechanical properties, specifically strength and stiffness, of technical hemp and flax fibers grown in Romania. Tensile testing was employed to determine stress-strain curves and the Young's modulus and to assess the failure strength of both fiber types. Although samples of various lengths were tested, no significant length-dependent variations were observed. However, a strong dependence on fiber diameter was noted, with the smallest diameters approaching the documented strength of elementary fibers. Due to the considerable variability in the experimental results pertaining to the characteristics of the reinforced fibers, a statistical analysis using a two-parameter Weibull distribution was employed. The analysis revealed three distinct stress-strain curve profiles, i.e., linear, bi-linear, and tri-linear patterns, with the average ultimate stress ranging from 412 to 566 MPa for hemp and 502 to 598 MPa for flax.