The Corrosion Fatigue Behavior and Mechanism of AerMet 100 Steel in 3.5% NaCl at Room Temperature

AerMet 100 steel is a new type of double-hardened high-strength steel, which is often used as landing gear material in amphibious aircraft. In the present paper, the corrosion fatigue behavior and mechanism of AerMet 100 high-strength steel in a 3.5% NaCl solution was studied by stress-controlled fatigue tests and a series of subsequent characterizations of the fracture surface, microstructure, and cracks. The results indicated that the fatigue life of AerMet 100 high-strength steel decreased with a decrease in the stress level in a 3.5% NaCl solution, satisfying the relationship lgN = -2.69 × 10^-3 σ + 6.49. The corrosion fatigue crack usually initiated from the corrosion pit and propagated across the martensitic flat noodles. Meanwhile, the corrosion fatigue crack tip was filled with Cr₂O₃, Fe₂O₃, and amorphous material; it propagated in the transgranular mode by a slip dissolution mechanism. This study provides some engineering significant for the fatigue performance of AerMet 100 steel in a 3.5% NaCl solution.