The Effect of Laponite on the Structure, Mechanical and Thermal Properties of Poly(butylene Succinate)

The comparison of some changes occurring in the physical properties of poly(butylene succinate) (PBS) due to its modification with Laponite (LAP) was the objective of this study. The PBS composites, containing from 1 to 7 wt% LAP, were prepared by co-rotating twin screw extrusion. The geometrical surface structure of the samples' fractures and the LAP content in the individual composites were examined. In addition, changes in the mechanical and thermal properties, melt flow rate and moisture sorption of the composites were studied. It was found that LAP increases the elastic modulus of PBS and also decreases its impact strength and, in particular, its strain. The strength of PBS changes to a lesser extent with an increase in the LAP content, i.e., it slightly decreases in tensile tests or slightly increases in bending tests. LAP also lowers the flow rate of PBS and significantly increases moisture sorption. Moreover, the composites produced were characterized by a uniform distribution of the dispersed phase in the polymer matrix and an acceptable adhesion at the interface between the two components.