Effect of Vanadium Addition on the Wear Resistance of Al_0.7CoCrFeNi High-Entropy Alloy

High-entropy alloys are of interest to many researchers due to the possibility of shaping their functional properties by, among other things, the use of alloying additives. One approach to improving the wear resistance of the AlCoCrFeNi alloy is modification through the addition of titanium. However, in this study, an alternative solution was explored by adding vanadium, which has a completely different effect on the material's structure compared to titanium. The effect of vanadium additives on changes in the microstructure, hardness, and wear resistance of the Al_0.7CoCrFeNi alloy. The base alloys Al_0.7CoCrFeNi and Al_0.7CoCrFeNiV_0.5 were obtained by induction melting. The results showed that the presence of vanadium changes the microstructure of the material. In the case of the base alloy, the structure is biphasic with a visible segregation of alloying elements between phases. In contrast, the Al_0.7CoCrFeNiV_0.5 alloy has a homogeneous solid solution bcc structure. The presence of vanadium increased hardness by 33%, while it significantly reduced friction wear by 73%. Microscopic observations of friction marks indicate differences in the wear mechanisms of the two materials.