Effect of Ti Doping of Al_0.7CoCrFeNi-Based High Entropy Alloys on Their Erosion Resistance by Solid Particles

The erosion resistance of materials against solid particles is a very important property, especially in the transportation of powders or in aeronautics (dust inside jet engines). There is a strong need to introduce new materials that have higher solid particle erosion resistance than state-of-the-art materials. Thus, in the present work, the solid erosion particles of high entropy alloys (HEAs) based on the Al0.7CoCrFeNi matrix were studied compared to the state-of-the-art stainless steel AISI 304. Furthermore, the effect of the addition of Ti to HEAs on hardness and erosion resistance was investigated. Current research included the development of the chemical composition of a new kind of HEA designed on the basis of thermodynamical calculations performed in CALPHAD, its manufacturing, full characterization involving microstructural and phase analyses, hardness measurements, solid particle erosion tests, and finally, the elucidation of erosion mechanisms. It was found that HEAs showed higher hardness as well as erosion resistance than AISI 304. Moreover, it was found that the increase in Ti content in an HEA resulted in an increase in the hardness and resistance to the erosion of the studied HEA. As the main reason for this phenomenon, the stabilization of the β-BCC phase, suppression of the α-FCC phase, and the appearance of the Ni₃Ti phase in the studied HEA were claimed.