Surface Roughness and Color Stability of Conventional and Bulk-Fill Resin Composite with S-PRG Fillers After Coffee...

This study aimed to evaluate the in vitro effects of coffee exposure on the color and roughness of conventional and bulk-fill resin composites, with and without surface pre-reacted glass-ionomer (S-PRG) filler.

Forty-eight cylindrical samples (Ø6 mm × 2 mm) were prepared and categorized as follows (n = 12 per group): conventional nano-hybrid (Tetric N-Ceram, Ivoclar); nano-hybrid with S-PRG filler (Beautifil II, Shofu); bulk-fill (Tetric N-Ceram Bulk Fill, Ivoclar); and bulk-fill with S-PRG filler (Beautifil Bulk Restorative, Shofu). The samples were assessed for surface roughness (Ra, μm), color coordinates (CIE Lab), and overall color change (ΔE_ab, ΔE₀₀). Measurements were taken at baseline and after 7 days of coffee immersion (pH = 4.95). Data were analyzed using generalized linear models, Kruskal-Wallis, Dunn, and paired Wilcoxon tests (α = 0.05).

After the coffee exposure, all resin composites exhibited a significant decrease in L* (towards black), an increase in a* (towards red), an increase in b* (towards yellow), and a higher Vita color score (p < 0.05). Tetric N-Ceram demonstrated the lowest roughness values post-exposure; however, a significant increase in roughness over time was observed only for Tetric N-Ceram Bulk Fill (p < 0.05). For ΔE_ab, Beautifil Bulk Restorative and Tetric N-Ceram showed higher values compared to Beautifil II. For ΔE₀₀, a significant difference was noted between Beautifil Bulk Restorative and Beautifil II (p < 0.05).

Resin composites with S-PRG fillers exhibited similar pigmentation dynamics to conventional composite but showed greater surface roughness after exposure to coffee. Considering the S-PRG materials, the bulk-fill version is more susceptible to staining.