Zn-doped CaP coating equips Ti implants with corrosion resistance, biomineralization, antibacterial and
Anca C Parau1, Senem Büyüksungur2, Guanhao Li3
1National Institute of Research and Development for Optoelectronics - INOE 2000, 409 Atomistilor St. 077125 Magurele, Romania.
Introduction:
Chronic inflammation leading to implant failure present major challenges in orthopedics, dentistry, and reconstructive surgery. Titanium alloys, while widely used, often provoke inflammatory complications. Zinc (Zn)-doped calcium phosphate (CaP) coatings offer potential to enhance implant integration by improving corrosion resistance, bioactivity, and immunocompatibility.
Objectives:
The objective of the study was to develope novel coating composition based on zinc-doped CaP coatings on Ti64 alloy implants that for the first time combines improved corrosion resistance, antibacterial properties and principally improved compatibility with the innate immunity primarily due to the proper programming of resident tissue macrophages to promote long-term implant acceptance.
Methods:
Ti64 substrates were coated with CaP and Zn-doped CaP using the microarc oxidation (MAO) technique. The adhesion between substrate and coatings are investigated by the progressive scratch test. The corrosion resistance and bioactivity were evaluated through electrochemical tests and simulated body fluid immersion. RNA sequencing was used to assess inflammatory responses in human primary macrophages. Antibacterial efficacy was tested against Escherichia coli and Staphylococcus aureus.
Results:
Zn addition significantly increased the adhesion of the coatings to Ti64 alloy, doubling up the critical load (from 4 N to 11 N). Zn-doped CaP coatings demonstrated enhanced corrosion resistance and increased biomineralization. RNA sequencing revealed that Zn addition suppressed inflammatory and promoted tolerogenic macrophage programming. Most pronounced effects was compensatory effect Zn on the CaP-supressed oxidative phosphorylation and lysosomal pathways in healing macrophages, and by upregulation of metallothioneins. Zn-doped coatings also exhibited superior antibacterial efficacy, reducing E. coli and S. aureus colonization by 99 % and 90 %, respectively.
Conclusion:
Zn-doped CaP coatings on Ti64 implants significantly improved corrosion resistance, bioactivity, and antibacterial performance. We developed an advanced multifunctional biomaterial equipped with beneficial anti-inflammatory and tissue integrative programming of innate immunity providing principal advantages for the long-term implant integration and reducing the implant failure risks.