High-Power Characteristics of Piezoelectric Transducers Based on [011] Poled Relaxor-PT Single Crystals

[011] poled relaxor-PT single crystals provide superior piezoelectric constants and electromechanical coupling factors in the 32 crystal directions, and also exhibit high electrical stability under compressive stresses and temperature changes. In particular, Mn-doped Pb(In_1/2Nb_1/2)O₃-Pb(Mg_1/3Nb_2/3)O₃-PbTiO₃ (Mn:PIN-PMN-PT) single crystals show a superior coercive field (E_C ≥ 8.0 kV/cm) and mechanical quality factor (Q_m ≥ 1030), making them suitable for high-power transducers. The high-power characteristics of [011] poled single crystals have been verified from a material perspective; thus, further investigation is required from a transducer perspective. In this study, the high-power characteristics of piezoelectric transducers based on [011] poled PIN-PMN-PT and [011] poled Mn:PIN-PMN-PT single crystals were investigated. To analyze the driving limits of the single crystals, the polarization-electric field (P-E) curves, as a function of the driving electric field, were measured. The results showed that [011] poled Mn:PIN-PMN-PT single crystals demonstrate lower energy loss and THD (Total Harmonic Distortion), directly relating to the driving efficiency and linearity of the transducer. Additionally, [011] poled Mn:PIN-PMN-PT crystals provide excellent stability under the compressive stress and temperature changes. To analyze the high-power characteristics of [011] poled single-crystal transducers, two types of barrel-stave transducers, based on [011] poled PIN-PMN-PT and [011] poled Mn:PIN-PMN-PT, were designed and fabricated. The changes in the impedance and transmitting voltage response with respect to the driving electric fields were measured, and the energy loss and THD of the transducers with respect to the driving electric fields were examined to assess the driving limit of the [011] poled single-crystal transducer. The high-power characteristic tests confirmed the stability of [011] poled Mn:PIN-PMN-PT single crystals and verified their potential for high-power transducer applications.