Mechanical Properties and σ-Phase Precipitation in FeCoCrNiMo_x (x = 0, 0.4, 0.5, 0.8, 1.3) High-Entropy Alloys:...

High-entropy alloys (HEAs) have garnered significant global interest due to their outstanding properties. This study investigates the structural stability and mechanical properties of FeCoCrNiMo_x (x = 0, 0.4, 0.5, 0.8, 1.3) HEAs using a first-principles approach coupled with the special quasi-random structure (SQS) method. Of the alloys examined, all except FeCoCrNiMo_1.3 were found to be thermodynamically and dynamically stable. Elasticity calculations revealed that molybdenum improves the ductility and anisotropy of the alloys, though with a slight decrease in strength and stiffness, as confirmed by electronic structure analysis. Defect-free FeCoCrNiMo_0.5 HEAs coatings were then prepared using laser cladding and characterized for their microstructure and hardness. The coating exhibited a transition from columnar crystals at the bottom to equiaxed crystals at the surface, forming a honeycomb-like structure. Inside the crystal cells, high-density dislocations and σ-phase were observed. Elasticity calculations of the σ-phase confirmed its high hardness, low ductility, and classification as a brittle, hard phase.