Platelet-Rich Fibrin Synthetic Bone Graft Enhances Bone Regeneration and Mechanical Strength in Rabbit Femoral...

This study evaluated the bone regeneration effect and mechanical properties of "Sticky bone", a mixture of platelet-rich fibrin (PRF) and synthetic bone grafts (SBGs), in the repair of large femoral bone defects in rabbits. Eighteen New Zealand white rabbits were included and randomly divided into a Sticky bone group and an SBG alone group. Bone graft samples were collected and analyzed at 4, 8, and 12 weeks after surgery. Micro- computed tomography (CT) analysis showed that the amount of the Sticky bone group in the grayscale ranges of 255-140 (highly mineralized tissue or unabsorbed bone powder) and 140-90 (representing new cancellous bone) was higher than that of the SBG group at each time point and decreased with the number of weeks. The compression strength test showed that the average compression strength of the Sticky bone group reached 5.17 MPa at the 12th week, which was 1.62 times that of the intact bone (3.19 MPa) and was significantly better than that of the SBG group (about 4.12 MPa). This study also confirmed for the first time that the use of a new polyethylene terephthalate (PET) blood collection tube to prepare PRF can stably release key growth factors such as platelet-derived growth factor-BB (PDGF-BB) and vascular endothelial growth factor (VEGF), which are conducive to early bone vascularization and cell proliferation. In summary, Sticky bone has the potential to promote bone formation, enhance tissue integration and mechanical stability, and can be used as an effective alternative material for repairing large-scale bone defects in clinical practice in the future.