Anodization and Its Role in Peri-Implant Tissue Adhesion: A Novel 3D Bioprinting Approach

Soft tissue stability around dental implant abutments is critical for maintaining a functional peri-implant seal. Yellow anodization is used to improve the aesthetic and surface characteristics of titanium abutments, yet its epithelial effects under more physiologically relevant 3D conditions remain insufficiently explored.

To develop a 3D bioprinted in vitro peri-implant mucosa model and to compare epithelial cell responses on yellow anodized versus turned titanium abutment surfaces.

Commercial Grade 5 (Ti6Al4V) titanium abutments were anodized and compared with turned controls. A collagen-based 3D bioprinted "collar-like" construct incorporating YD-38 epithelial cells was fabricated using a custom holder system to simulate peri-implant mucosal contact. Samples were cultured for 14 and 21 days. Cell distribution and morphology were assessed by optical microscopy and HE staining, while cytoskeletal organization was evaluated by TRITC-phalloidin/Hoechst staining and confocal microscopy. Quantitative fluorescence analysis was performed at 21 days.

Both surfaces supported epithelial coverage in the 3D environment. Anodized specimens showed more pronounced actin cytoskeletal organization and the presence of actin-rich, filamentous cellular extensions compared with turned controls. Quantitative image analysis demonstrated significantly higher TRITC-phalloidin signal intensity at 21 days on anodized samples (p < 0.001).

Within the limitations of a 3D epithelial in vitro model using YD-38 cells, yellow anodization was associated with enhanced epithelial cytoskeletal organization compared with turned titanium. The presented 3D bioprinted platform may serve as a practical in vitro tool for screening abutment surface modifications relevant to peri-implant soft tissue integration.