Innovative Application of Electroslag Remelting in Inclusion Removal from Silicon Alloys and Silicon Recovery from...

The rapid expansion of crystalline silicon photovoltaic (PV) modules has increased the demand for sustainable and high-value recycling strategies for end-of-life (EOL) modules. A significant challenge is the removal of impurities such as carbon, oxygen, and non-metallic inclusions introduced into silicon solar cells during the dissociation of PV laminates. To address this, we propose a non-consumable electrode electroslag remelting (NCE-ESR) process to effectively eliminate inclusions. In this process, the reverse flow of alloy droplets and the extensive contact area are crucial during the reverse flow slag washing. Initially, we studied the occurrence characteristics of inclusions in silicon solar cells obtained after pyrolysis from enterprises. Pyrolysis facilitated the formation of inclusions like Si-O, C-O, Al-O, and Si-N, particularly in the fine size range below 5 μm. To enhance impurity removal, the recycled Si was alloyed with Cu, which increased the melt density and impurity activity. Based on optimized thermodynamics and physical properties, we designed a novel electroslag composition of 40%CaO-40%SiO₂-20%CaF₂ suitable for silicon alloy refining. Notably, during the reverse flow slag washing of the Cu-Si alloy, the maximum removal rate of inclusions reached 77.42%. The average diameter of inclusions was reduced to below 6 μm, and the removal rates of impurity elements such as Al, O, and C exceeded 98.09%, 94.86%, and 86.08%, respectively. Finally, we independently developed the NCE-ESR equipment and conducted a kilogram-scale amplification test. The results indicated that the impurity removal rates of Al and O exceeded 97%, and the final inclusion size was less than 10 μm. This study demonstrates a scalable and environmentally friendly approach for the high-value recycling of silicon resources from decommissioned PV modules.