Magnetic Composites for Advanced Characterization of Magnetic Field Sensors and Biosensors

Gadolinium is a rare-earth element that is promising for the field of biomedicine due to its unique properties that enhance image quality, giving it high potential in targeted cancer therapy, antimicrobial treatments, etc. The disadvantage of Gd-containing materials is their high toxicity. In this work, ensembles of Fe and Al₂O₃ nanoparticles were fabricated by the electric explosion of wire and Gd ribbons using rapid quenching techniques. Stable Fe, Fe/Gd and Fe/Gd/Al₂O₃ aqueous suspensions with a Z-potential of about -54 mV were fabricated by the ball-milling mechanosynthesis of Fe (100%), Fe and Gd (70 and 30 wt. % accordingly) and Fe, Al₂O_3, and Gd (69, 30 and 1 wt.% accordingly). Fillers from suspensions were used for the synthesis of epoxy composites mimicking natural tissue with embedded magnetic particles. The concentration range for synthesized epoxy composites (0, 5, 10, and 15 wt.% of the filler) corresponded to the biomedical range of interest. Thin-film magnetoimpedance (MI) elements were prepared by a sputtering technique: conventional [FeNi/Cu]₅/Cu/[Cu/FeNi]₅ (NP) element and [FeNi/Cu]₅/Cu/[Cu/P{FeNi]₅} element with patterned top multilayer (SqP). They showed a maximum MI ratio of about 160% for NP and about 60% for SqP. MI sensor response was affected by the presence of filled magnetic composites in the shape of cylinders (5 mm × 4 mm) situated at about 1 mm due to the stray fields in the filler. MI response showed a linear dependence on the filler concentration for each selected position. These results open the possibility to develop new iron- and gadolinium-containing materials for simultaneous magnetic imaging and detection by magnetic field sensors, extending the functional properties of Fe/Gd materials for biomedical devices and therapies.