Alkali Activation of Natural Calcium Bentonite for Foundry Applications: Structural, Physicochemical, and...

The technological performance of bentonite in foundry applications is strongly influenced by the nature of its exchangeable interlayer cations, with sodium bentonites generally exhibiting superior swelling, plasticity, and bonding properties compared with calcium bentonites. Given the limited availability of natural sodium bentonite, upgrading abundant calcium-rich bentonite resources holds significant industrial interest. In this study, a natural Ca-rich bentonite from the Bijelo Polje deposit (Bar, Montenegro) was upgraded by alkali activation using Na₂CO₃ and evaluated as a binder for green sand foundry molds. The raw bentonite was characterized by physicochemical, mineralogical, and structural analyses, confirming its Ca-type character and suitability for sodium activation. Activation was performed using 2-6 wt.% Na₂CO₃, with the optimum treatment achieved at 5 wt.% Na₂CO₃. The activated bentonite was subsequently characterized using structural, textural, thermal, and physicochemical methods. Alkali activation significantly improved the key technological properties of the material, increasing the free swelling capacity from 7 to 20 cm³, the specific surface area from 27.4 to 45.8 m² g^-1, the cation exchange capacity from 74.6 to 89.5 meq/100 g, and the plasticity index from 79.6% to 193.4%. XRD, ATR-FTIR, and thermal analyses confirmed successful sodium activation while preserving the fundamental montmorillonite structure. Evaluation of foundry-relevant properties, including refractoriness, methylene blue adsorption, gas permeability, thermal stability, and bonding strength, demonstrated that the activated bentonite satisfies the technological requirements for green sand molding of both ferrous and non-ferrous alloys. These findings demonstrate that Na₂CO₃ activation is an effective and resource-efficient approach for converting natural Ca-rich bentonite into a high-performance foundry binder.