Sustainable Development and Polymer-Based Functional Innovation in the Lacquer Industry: Resources, Technologies, and...

Natural lacquer, a bio-based polymer derived from Toxicodendron vernicifluum, has attracted renewed scientific interest as a sustainable coating material with exceptional mechanical durability, chemical resistance, and aesthetic qualities. This review synthesizes current knowledge on the chemical composition, enzymatic curing mechanisms, and structure-property relationships of lacquer-based polymer systems, with particular focus on recent advances in functional modification and processing technology. Key findings indicate that laccase-catalyzed oxidative polymerization, operating optimally at pH 6.0-7.5 and 20-30 °C, governs the formation of a highly cross-linked urushiol network whose properties are fundamentally determined by side-chain unsaturation and emulsion stability. Mechanistic analysis reveals that polyurethane hybridization improves weathering resistance by introducing flexible aliphatic segments and additional hydrogen-bonding cross-links, while graphene oxide incorporation enhances anticorrosion performance through a physical barrier mechanism that prolongs ionic diffusion pathways. UV-curable LPEA derivatives achieve an 83% reduction in curing time relative to ambient-cured lacquer, enabling integration with industrial spray-coating lines. Despite these advances, several critical limitations remain inadequately resolved. Allergen reduction strategies have not yet achieved sufficient quantitative efficiency for large-scale commercial deployment, and the long-term stability of nanocomposite lacquer films under sustained UV exposure and hydrothermal conditions is not well established. Furthermore, most high-performance modification systems reported in the literature are demonstrated only on laboratory scale, with scalability, substrate compatibility, and lifecycle performance remaining largely unvalidated. The review identifies the absence of standardized performance evaluation protocols and the fragmentation of structure-property data across studies as key barriers to systematic progress, and proposes that future work prioritize the development of integrated processing-modification-performance frameworks to guide the rational design of next-generation lacquer-based functional materials.