Flexural properties of denture-base polymer reinforced with glass-fibre polysulphone composite

The aim of this study was to determine the effect of glass-fibre composite reinforcement on the flexural strength and flexural modulus poly-methyl methacrylate (PMMA). Prefabricated electrical glass-fibre polysulphone composite rods (GF/PSu), 3mm in diameter, were incorporated in cylindrical, heat polymerizing PMMA specimens with diameters of 4, 5 and 6mm respectively (n = 10). These specimens were compared with PMMA control groups of similar dimension. A three point loading test was performed in air after storage of specimens in water at 37 degrees C for 8 weeks. The following variables were measured : Flexural Strength (FS) and Flexural Modulus (FM). The data were analyzed using one way analysis of variance (ANOVA). After testing, the fracture zone was evaluated using a scanning electron microscope (SEM). The glass-fibre reinforcement used in this study significantly enhanced both the FM and FS values of PMMA. This enhancement was, however, progressively reduced in relation to an increase in cross-sectional dimension of the specimens. SEM evaluation revealed delamination and fracture of the glass-fibres in the polymer matrix.