Shape-tunable Pt-Ir alloy nanocatalysts with high performance in oxygen electrode reactions
Tao Zhang1, Shuai-Chen Li1, Wei Zhu1
1Beijing National Laboratory for Molecular Sciences, State Key Laboratory of Rare Earth Materials Chemistry and Applications, PKU-HKU Joint Laboratory in Rare Earth Materials and Bioinorganic Chemistry, College of Chemistry and Molecular Engineering, Peking University, Beijing 100871, China. ywzhang@pku.edu.cn.
Abstract:
For the first time, shape-tunable Pt-Ir alloy nanocatalysts including both single-crystalline (nano-octahedra (NOs), nano-truncated octahedra (NTOs), nanocubes (NCs)) and polycrystalline (nanocluster flowers (NCFs), nanowires (NWs), nano-short-chains (NSCs), and nano-octahedral stars (NOSs)) ones were synthesized with a facile one-pot solvothermal method, via precise control of the facet-selective agents (Br- and I-). The surface effects of Pt-Ir alloy nanocatalysts for oxygen electrode reaction in acidic solution were intensively investigated. Pt-Ir alloy nanocatalysts showed enhanced catalytic activities for the oxygen evolution reaction (OER), which were 1.6 to 2.0 times those of the commercial Ir/C catalyst and the Pt/C-Ir/C mixture at an overpotential of 0.25 V. The catalytic activity for the OER exhibited a positive correlation with the proportion of surface IrOx species, but was restricted by the surface alloying effect. Besides the change of the intermediate adsorption state, the dissociation of water was also confirmed to be effective as the rate-determining step of the Pt-Ir alloy nanocatalysts. The catalytic activity for the oxygen reduction reaction (ORR) decreased with the increase of surface IrOx species. Pt-Ir nano-short-chains (NSCs) exhibited 1.3 times the catalytic activity as that of the commercial Pt/C catalyst at 0.80 V and 0.85 V, owing to the higher proportion of the (110) facets with irregular step sites exposed after the annealing treatment at 350 °C. The unique structure could prevent the mass transfer process from being obstructed by adsorbed bisulfate anions and oxidized species on the surfaces. Pt-Ir NSCs exhibited a catalytic efficiency of 46.7% and were considered to be a promising URFC catalyst.
Related Concept Videos
01:22Heterogeneous Catalysis
02:44Oxidation of Alkenes: Syn Dihydroxylation with Osmium Tetraoxide
02:17Reduction of Alkenes: Asymmetric Catalytic Hydrogenation
The metal catalyst used can be either heterogeneous or homogeneous. When hydrogenation of an alkene generates a chiral center, a pair of enantiomeric products is expected to form. However, an enantiomeric excess of one of the products can be facilitated using an enantioselective reaction or an...
01:46Oxidative Cleavage of Alkenes: Ozonolysis
Ozone is a symmetrical bent molecule stabilized by a resonance structure.
02:13Reduction of Alkenes: Catalytic Hydrogenation
Metals like palladium, platinum, and nickel are commonly used in their solid forms — fine powder on an inert surface. As these catalysts remain insoluble in the reaction mixture, they are referred to as heterogeneous catalysts.
The hydrogenation process takes place on the...