Infiltration of Solution-Processable Solid Electrolytes into Conventional Li-Ion-Battery Electrodes for...

Bulk-type all-solid-state lithium-ion batteries (ASLBs) have the potential to be superior to conventional lithium-ion batteries (LIBs) in terms of safety and energy density. Sulfide SE materials are key to the development of bulk-type ASLBs because of their high ionic conductivity (max of ∼10^-2 S cm^-1) and deformability. However, the severe reactivity of sulfide materials toward common polar solvents and the particulate nature of these electrolytes pose serious complications for the wet-slurry process used to fabricate ASLB electrodes, such as the availability of solvent and polymeric binders and the formation of ionic contacts and networks. In this work, we report a new scalable fabrication protocol for ASLB electrodes using conventional composite LIB electrodes and homogeneous SE solutions (Li₆PS₅Cl (LPSCl) in ethanol or 0.4LiI-0.6Li₄SnS₄ in methanol). The liquefied LPSCl is infiltrated into the tortuous porous structures of LIB electrodes and solidified, providing intimate ionic contacts and favorable ionic percolation. The LPSCl-infiltrated LiCoO₂ and graphite electrodes show high reversible capacities (141 and 364 mA h g^-1) at 0.14 mA cm^-2 (0.1 C) and 30 °C, which are not only superior to those for conventional dry-mixed and slurry-mixed ASLB electrodes but also comparable to those for liquid electrolyte cells. Good electrochemical performance of ASLBs employing the LPSCl-infiltrated LiCoO₂ and graphite electrodes at 100 °C is also presented, highlighting the excellent thermal stability and safety of ASLBs.