Effects of Curing Modes on the Microhardness of Resin-modified Glass Ionomer Cements

This study evaluated the effects of curing modes on surface microhardness of visible light-cured resin-modified glass ionomer cements (VLC RMGIC) and a giomer after different storage periods in comparison to auto-cured resin-modified glass ionomer cements (AC RMGIC).

The following materials were used: VLC RMIC: Fuji II LC Improved, Photac Fil Quick Aplicap, AC RMGIC: Fuji Plus, Fuji VIII and Giomer: Beautifil II. The measurements of microhardness were performed using a Vickers test (100 g loads were applied for 10 s) in the following time intervals: immediately after the recommended cure and after 1, 7 and 14 days of immersion in distilled water. Five samples (d=4 mm, h=2 mm) were prepared for each combination of curing mode and tested material.

After 14 days, an improvement of microhardness was evident in all tested materials. The full factorial ANOVA identified a highly significant (p<0.001) effect of the factors "material", "time" and "curing mode ("low", "soft", "high") for the light-cured materials Beautifil II, Fuji II LC and Photac Fil Quick. There was a statistically significant difference in the microhardness between different material types (Beautifil II˃Fuji II LC˃Photac Fil Quick˃Fuji Plus˃Fuji VIII) and curing modes (low ˂soft ˂high).

Material type had the greatest impact on microhardness, followed by the factor of time, while curing modes showed a considerably smaller influence on microhardness of the light-cured materials.