Radiopacity of resin-based CAD/CAM blocks assessed by areal grayscale pixel value measurement

This study assessed radiopacity of resin-based computer-aided-design/computer-aided-manufacturing (CAD/CAM) materials by areal grayscale pixel value measurement.

Radiopacities of six resin-based CAD/CAM block materials and resin composite were evaluated and compared to that of enamel and dentin. Specimens of 1-mm thickness were placed on photostimulable phosphor plate and irradiated with digital x-ray unit. On the radiographic image, regions of interests were determined for each specimen and areal grayscale pixel values were measured. Elemental analysis was performed with energy-dispersive x-ray spectroscopy (EDS) on field emission scanning electron microscope (FESEM) images of the specimens. Data were analyzed statistically (α = 0.05).

Radiopacity values of the restorative materials were significantly different from each other (P < 0.05). Radiopacity values of two resin-based CAD/CAM materials were significantly lower than that of dentin (P < 0.05). All tested restorative materials contain zirconium, three materials contain barium, and only resin composite contains lanthanum.

Four CAD/CAM materials with higher amounts of zirconia or barium (>18%) had radiopacity values significantly higher than the dentin; while two materials with lower amounts of zirconia (<4%) and/or no-barium, had radiopacity values significantly lower than the dentin. EDS analysis suggests materials containing elements with higher atom numbers such as zirconia and barium could exhibit higher radiopacity.