Highly Porous 3D Printed Tantalum Scaffolds Have Better Biomechanical and Microstructural Properties than Titanium
Huaquan Fan1, Shu Deng1, Wentao Tang2
1Center for Joint Surgery, Southwest Hospital, Third Military Medical University, No. 29 Gaotanyan Street, Shapingba District, Chongqing 400038, China.
Objective:
To test the biomechanical properties of 3D printed tantalum and titanium porous scaffolds.
Methods:
Four types of tantalum and titanium scaffolds with four alternative pore diameters, #1 (1000-700 μm), #2 (700-1000 μm), #3 (500-800 μm), and #4 (800-500 μm), were molded by selective laser melting technique, and the scaffolds were tested by scanning electronic microscope, uniaxial-compression tests, and Young's modulus tests; they were compared with same size pig femoral bone scaffolds.
Results:
Under uniaxial-compression tests, equivalent stress of tantalum scaffold was 411 ± 1.43 MPa, which was significantly larger than the titanium scaffolds (P < 0.05). Young's modulus of tantalum scaffold was 2.61 ± 0.02 GPa, which was only half of that of titanium scaffold. The stress-strain curves of tantalum scaffolds were more similar to pig bone scaffolds than titanium scaffolds.
Conclusion:
3D printed tantalum scaffolds with varying pore diameters are more similar to actual bone scaffolds compared with titanium scaffolds in biomechanical properties.
More Related Videos
06:12Plasma Polishing as a New Polishing Option to Reduce the Surface Roughness of Porous Titanium Alloy for 3D Printing
Published on: April 28, 2023
09:35Distinctive Capillary Action by Micro-channels in Bone-like Templates can Enhance Recruitment of Cells for Restoration of Large Bony Defect
Published on: September 11, 2015