Analysis of Microstructure Evolution and Mechanical Properties during Compression of Open-Cell Ni-Foams with Hollow...

Based on electron backscatter diffraction (EBSD), hollow structures of Ni foam struts fabricated by electroplating on a chemically removable template were observed. Three-dimensional (3D) pore structures of Ni foams were also obtained using X-ray computed tomography (CT), and microstructural features such as porosity, pore size and strut thickness were statistically quantified. Evolution of microstructure and mechanical properties during ex situ compression of open-cell Ni-foams was investigated based on X-ray CT, and experimental results were compared with predictions by the finite element method (FEM). 3D microstructures obtained by X-ray CT revealed that the stress drop started with the buckling of struts at the center of the Ni-foams. The flow stress increased after the buckling of the struts spreads to most of the regions. For effective simulation of the compressive deformation and determination of the microstructural evolution, small domains of interest were selected from the entire set of observed 3D microstructures based on X-ray CT, and struts of Ni foams with a hollow structure were simplified with relevant thin-solid struts. Numerical 3D modeling comprehensively disclosed that compression caused the transverse buckling of the struts, with the bending and buckling of struts thus reducing the stress. Thickness variation of the struts causes a change in the porosity of Ni-foams without a change in pore shape or connectivity. The overall range of strut thickness was from 59 to 133 μm, and the range of porosity values was from 80% to 93.7%. A stress drop was predicted with a decrease in the strut thickness or an increase in the porosity, as measured experimentally. It was also found that the stress drop contributed to an increase in the calculated energy absorption efficiency.