Is the Er:YAG laser affect the surface characteristics and bond strength of Y-TZP?

This study evaluated the surface characteristics and bond strength of Y-TZP treated with Er:YAG laser at different focal distances. 120 Y-TZP blocks were divided into five groups (n=24), according to the surface treatment: no treatment (C-); sandblasting with silica-coated aluminum oxide particles (C+); and Er:YAG laser application at focal distances of 1mm (Er:YAG-1), 4mm (Er:YAG-4), and 7mm (Er:YAG-7). Surface characteristics were analyzed using Vickers microhardness, confocal laser microscope, scanning electron microscopy (SEM), and X-ray diffractometer (XRD). For the bond strength test, 100 Y-TZP blocks were subdivided into two subgroups (n=10), according to the resin cement used: with (MDP+) or without 10-methacryloyloxydecyl dihydrogen phosphate (MDP-). The Vickers microhardness and surface roughness were analyzed by one-way ANOVA and bond strength by two-way ANOVA and Tukey's test for both (α=0.05). Vickers microhardness differences were not observed between the groups (p>0.05); C+ showed higher surface roughness values. SEM images showed micromorphological differences between the groups. The XRD data detected tetragonal crystals for C- and, for the other groups, tetragonal and monoclinic peaks. For bond strength, no statistically difference significance were observed among the cements with or without MDP (p>0.05) but showed significant difference between the surface treatments (C+ > C- = Er:YAG1 > Er:YAG4 = Er:YAG7) (p<0.05). Suggested that the Er:YAG laser cannot replace conventional treatment with aluminum oxide particles and the presence of MDP in the resin cement had no influence on the bond strength.