Critical conditions for the formation of p-type ZnO with Li doping

Mingge Jin1,2, Zhibing Li1, Feng Huang2

  • 1State Key Laboratory of Optoelectronic Materials and Technologies, School of Physics, Guangdong Province Key Laboratory of Display Material and Technology, Sun Yat-sen University Guangzhou 510275 People's Republic of China wangwl2@mail.sysu.edu.cn.

RSC Advances
|May 13, 2022
PubMed

More Related Videos

Aerosol-assisted Chemical Vapor Deposition of Metal Oxide Structures: Zinc Oxide Rods06:39

Aerosol-assisted Chemical Vapor Deposition of Metal Oxide Structures: Zinc Oxide Rods

Published on: September 14, 2017

13.3K
Fabrication of Schottky Diodes on Zn-polar BeMgZnO/ZnO Heterostructure Grown by Plasma-assisted Molecular Beam Epitaxy14:16

Fabrication of Schottky Diodes on Zn-polar BeMgZnO/ZnO Heterostructure Grown by Plasma-assisted Molecular Beam Epitaxy

Published on: October 23, 2018

7.8K

Related Concept Videos

P-N junction01:11

P-N junction

A p-n junction is formed when p-type and n-type semiconductor materials are joined together. At the interface of the p-n junction, holes from the p-side and electrons from the n-side begin to diffuse into the opposite sides due to the concentration gradient. This diffusion of carriers leads to a region around the junction where there are no free charge carriers, known as the depletion region. The charge density within the depletion region for the n-side and p-side can be described by the...
Imperfections in Crystal Structure: Stoichiometric Point Defects01:26

Imperfections in Crystal Structure: Stoichiometric Point Defects

Schottky defects arise when some lattice points in a crystal, such as those in NaCl, remain unoccupied, creating lattice vacancies without disturbing the overall electrical neutrality of the crystal. This defect is common in ionic crystals where the positive and negative ions are similar in size, as seen in sodium chloride and cesium chloride. The presence of Schottky defects enables the crystal to conduct electricity to a small extent through an ionic mechanism. Electric fields cause nearby...