Comparative Evaluation of the Remineralization Potential of Fluoride-containing Toothpaste, Honey Ginger Paste and
Kimaya K Kade1, Shweta Chaudhary1, Rohan Shah1
1Department of Pediatric and Preventive Dentistry, Bharati Vidyapeeth Dental College and Hospital (Deemed to be University), Pune, Maharashtra, India.
Introduction:
A drop in pH of the oral cavity results in demineralization, which, if continued, leads to loss of minerals from tooth structure, resulting in dental caries. A goal of modern dentistry is to manage noncavitated caries lesions noninvasively through remineralization in an attempt to prevent disease progression.
Materials And Methods:
A total of 40 extracted premolar teeth were selected for the study. The specimens were divided into four groups, group I, the control group; group II, remineralizing agent as fluoride toothpaste; group III, the treatment material as ginger and honey paste; and group IV, the treatment material as ozone oil. An initial reading of surface roughness and hardness was recorded for the group (control group). Repeated treatment has continued lasting 21 days. This saliva was changed each day. Following the lesion formation procedure, the surface microhardness was measured for all specimens. The parameters were 200 gm force for 15 seconds with a Vickers indenter and the roughness of the demineralized area of each specimen was obtained by using the surface roughness tester.
Results:
Surface roughness was checked by using a surface roughness tester. Before starting the pH cycle, the baseline value for the control group was calculated. The baseline value for the control group was calculated. The surface roughness average value for 10 samples is 0.555 µm and the average surface microhardness is 304 HV; the average surface roughness value for fluoride is 0.244 µm and the microhardness is 256 HV, 0.241 µm, and 271 HV value for honey-ginger paste. For ozone surface roughness average value is 0.238 µm and the surface microhardness average mean value is 253 HV.
Conclusion:
The future of dentistry will rely on the regeneration of tooth structure. There is no significant difference seen between each treatment group. Considering the adverse effect of fluoride, we can consider honey-ginger and ozone as good remineralizing agents for fluoride.